Tratamiento de superficie de las restauraciones de porcelana feldespática y su implicancia en la propagación de las fallas estructurales propias del material

Surface treatment of feldespathic porcelain restoration and its implication in the spread of the material's structural failures


Universidad Nacional de Cuyo. Facultad de Odontología enviar el email al autor

Colaboradores: Ventrera, Verónica Co-autor/a
Carrazco, María Elizabeth Co-autor/a


Publicado en el en Revista de la Facultad de Odontología (Vol. 8, no. 2)
Institución Editora: Universidad Nacional de Cuyo. Facultad de Odontología Idioma: Español


Resumen:

Español
Durante el proceso de elaboración de las porcelanas feldespáticas se producen en su interior micro rajaduras las cuales se propagan a través de la matriz vítrea aumentando la fragilidad del material cuando se lo expone a los esfuerzos mecánicos. Las restauraciones rígidas de porcelanas feldespáticas son sometidas a distintos tratamientos en su superficie para aumentar la adhesión a las estructuras dentarias cuando son cementadas. Estos tratamientos son acondicionamiento con ácido fluorhídrico y microarenado. Objetivos de este trabajo: 1. Evaluar la resistencia flexural de este material mediante ensayo mecánico en máquina Instron, previo tratamiento en su superficie con ácido fluorhídrico y microarenado. 2. Observar al MEB las alteraciones de superficie producidas por el microarenado y el ácido fluorhídrico. Los resultados obtenidos demostraron que el tratamiento de microarenado produjo una reducción de la resistencia flexural. El MEB confirmó la presencia de mayor cantidad de microgrietas que podrían ser responsables de la disminución de la resistencia flexural.

Inglés
In the preparation of feldspathic porcelains occur within microcracks, which propagate through the glass matrix making them very fragile when they are required mechanically. The aim of this study was to evaluate the flexural strength of feldspathic porcelain after being treated with sandblasting and hydrofluoric acid. The samples were viewed with SEM to observe that these two treatments altered form the porcelain surface. Ceramic samples were prepared on which surface treatment is performed with hydrofluoric acid and sandblasting. The samples thus prepared were subjected to an Instron to determine the flexural strength. The result was that the sandblasting treatment produced a highly significant reduction in flexural strength. SEM confirmed the presence of as many microgrietas responsible for the decrease in flexural strength.


Disciplinas:
Odontología

Palabras clave:
Porcelana feldespática - Microarenado - Microgrietas - Resistencia flexural

Descriptores:
PORCELANA DENTAL - ÁCIDO FLUORHÍDRICO - RESTAURACIÓN DENTAL PERMANENTE

descargar pdf


Licencia Creative Commons

Este obra está bajo una Licencia Creative Commons Atribución-NoComercial-CompartirIgual 3.0 Unported.
Conozca más sobre esta licencia >

Cómo citar este artículo:

Barrionuevo, María Eugenia Alejandra (2014) "Tratamiento de superficie de las restauraciones de porcelana feldespática y su implicancia en la propagación de las fallas estructurales propias del material: ". En: Revista de la Facultad de Odontología, Vol. 8, no. 2, p. 8-11.
Dirección URL del artículo: https://bdigital.uncu.edu.ar/7277.
Fecha de consulta del artículo: 31/10/20.
Cómo incrustar el enlace a este documento en tu sitio

<iframe src="/app/widget/?idobjeto=7277&tpl=widget" width="420px" frameborder="0" ></iframe>